                                 CHINA ISO Sillica gel adsorbent

 CHINA ISO Sillica gel adsorbent Product Details:

        Kiselgel A including pore spherical silica gel and pore bulk silica gel has a transparent or translucent appearance with average pore diameter 2.0-3.0nm,specific surface 650-800m2/g, pore volume 0.35-0.45ml/g, specific heat 0.92KJ/kg. ?, thermal conductivity 0.63KJ/m.Hr.?. . Pore silica gel is also called silica gel A.


  Material: made of food grade silica gel, 100% new can be through the RoHS, Reach, SGS, FDA and LFGB testing, etc.
Size: 26 x19. 5 cm
Weight: 50 grams, lighter, let baby wear more comfortable.

Kiselgel A including pore spherical silica gel and pore bulk silica gel has a transparent or translucent appearance with average pore diameter 2.0-3.0nm,specific surface 650-800m2/g, pore volume 0.35-0.45ml/g, specific heat 0.92KJ/kg. ?, thermal conductivity 0.63KJ/m.Hr.?. . Pore silica gel is also called silica gel A.

CHINA ISO Sillica gel adsorbent Technical Index:

Items		Index			Standard numerical value
		Superior product	Top quality product	Qualified product
Absorbing capacity	RH=20%,% =	8.0	7.0	6.0	11.2
	RH=50%,% =	20.0	19.0	18.0	29.2
	RH=90%,% =	30.0	29.0	28.0	37.6
Heating loss% =		2.0	4.0	6.0	1.0
PH value		4-8	--	--	4
Specific resistance ONaN =		3000	--	--	5630
Silica content% =		98	--	--	98.5
Qualified rate of spherical particles % =		82	--	--	90
Particle size		Protocol	Protocol	Protocol	2-5mm
Stacking density g/L		Protocol	Protocol	Protocol	784
Note: qualified rate of spherical particles is only applicable to pore spherical particles.

CHINA ISO Sillica gel adsorbent Application:

Mainly used for drying, moisture proof, also used as catalyst carriers, adsorbents, separating agent, and pressure swing adsorption.

CHINA ISO Sillica gel adsorbent Standard Packaging:

25 Kg/Bag

CHINA ISO Sillica gel adsorbent Attention: 
·The product cannot be exposed in the open air and should be stored in dry condition with air-proof package.
·The product should be regenerated after a certain period of adsorption. The appropriate regenerated temperature would be better below 350?.